Hydroxyapatite/titania sol-gel coatings on titanium-zirconium alloy for biomedical applications

A simple sol–gel method was developed for hydroxyapatite/titania (HA/TiO2) coatings on non-toxic titanium–zirconium (TiZr) alloy for biomedical applications. The HA/TiO2-coated TiZr alloy displayed excellent bioactivity when soaked in a simulated body fluid (SBF) for an appropriate period. Differential scanning calorimetry, thermogravimetric analysis, X-ray diffraction and scanning electron microscopy-energy dispersive spectrometry were used to characterize the phase transformations and the surface structures and to assess the in vitro tests. The HA/TiO2 layers were spin-coated on the surface of TiZr alloy at a speed of 3000 rpm for 15 s, followed by a heat treatment at 600 °C for 20 min in an argon atmosphere sequentially. The TiO2 layer exhibited a cracked surface and an anatase structure and the HA layer displayed a uniform dense structure. Both the TiO2 and HA layers were 25 μm thick, and the total thickness of the HA/TiO2 coatings was 50 μm. The TiZr alloy after the above HA/TiO2 coatings displayed excellent bone-like apatite-forming ability when soaked in SBF and can be anticipated to be a promising load-bearing implant material.

Comparison of tissue dosimetry in the mouse following chronic exposure to arsenic compounds

Several chronic bioassays have been conducted in multiple strains of mice in which various concentrations of arsenate or arsenite were administered in the drinking water without a tumorigenic effect. However, one study (Ng et al., 1999) reported a significant increase in tumor incidence in C57Bl/6J mice exposed to arsenic in their drinking water throughout their lifetime, with no tumors reported in controls. A physiologically based pharmacokinetic model for arsenic in the mouse has previously been developed (Gentry et al., 2004) to investigate potential differences in tissue dosimetry of arsenic species across various strains of mice. Initial results indicated no significant differences in blood, liver, or urine dosimetry in B6C3F1 and C57Bl/6 mice for acute or subchronic exposure. The current work was conducted to compare model-predicted estimates of tissue dosimetry to additional kinetic information from the (C57Bl/6 x CBA)F1 and TgAc mouse. The results from the current modeling indicate that the pharmacokinetic parameters derived based on information in the B6C3F1 mouse adequately describe the measured concentrations in the blood/plasma, liver, and urine of both the (C57Bl/6 x CBA)F1 and TgAc mouse, providing further support that the differences in response observed in the chronic bioassays are not related to strain-specific differences in pharmacokinetics. One significant finding was that no increases in skin or lung concentrations of arsenic species in the (C57Bl/6 x CBA)F1 strain were observed following administration of low concentrations (0.2 or 2 mg/L) of arsenate in the drinking water, even though differences in response in the skin were reported. These data suggest that pharmacodynamic changes may be observed following exposure to arsenic compounds without an observable change in tissue dosimetry. These results provided further indirect support for the existence of inducible arsenic efflux in these tissues.

Sol-gel derived HA/TiO2 double coatings on Ti scaffolds for orthopaedic applications

Hydroxyapatite/titania (HA/TiO₂) double layers were coated onto Ti scaffolds throughout for orthopaedic applications by sol-gel method. Differential scanning calorimetry (DSC), thermogravimetric analysis (TG) and X-ray diffractometry (XRD) were used for the characterisation of the phase transformations of the dried gels and coated surface structures. Scanning electron microscope (SEM) equipped with energy dispersive spectrometry (EDS) was used for the observation and evaluation of the morphology and phases of the surface layers and for the assessment of the in vitro tests. The in vitro assessments were performed by soaking the HA/TiO₂ double coated samples into the simulated body fluid (SBF) for various periods. The TiO₂ layer was coated by a dipping-coating method at a speed of 12 cm/min, followed by a heat treatment at 600 °C for 20 min. The HA layer was subsequently dipping-coated on the outer surface at the same speed and then heat-treated at difference temperatures. The results indicat that the HA phase begins to crystallize after a heat treatment at 560 °C. The crystallinity increases obviously at 760 °C. SEM observations find no delamination or crack at the interfaces of HA/TiO₂ and TiO₂/Ti. The HA/TiO₂ coated Ti scaffolds displays excellent bone-like apatite forming ability when it is soaked into SBF. Ti scaffolds after HA/TiO₂ double coatings can be anticipated as promising implant materials for orthopaedic applications

Sol-gel derived hydroxyapatite/titania biocoatings on titanium substrate

A simple sol–gel method was successfully developed for a hydroxyapatite (HA)/TiO₂ double layer deposition on a pure titanium substrate. Phase formation, surface morphology, and interfacial microstructure were investigated by differential scanning calorimetry analysis (DSC), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The TiO₂ layer was coated by a spin coating method at a speed of 1500 rpm for 15 s, followed by a heat treatment at 560 °C for 20 min. The HA film was subsequently spin coated on the outer surface at the same speed and then heat-treated at difference temperatures. Results indicated that the HA phase began to crystallize after a heat treatment at 580 °C; and the crystallinity increased obviously at a temperature of 780 °C. The HA film showed a porous structure and a thickness of 5–7 μm after the heat treatment at 780 °C. SEM observations revealed no delamination and crack at the interfaces of HA/TiO₂ and TiO₂/Ti. The HA film with a porous structure is expected to be more susceptible to the natural remodeling processes when it is implanted in a living body.

Photo-catalysis of red wine stains using titanium dioxide sol-gel coatings on wool fabrics

This paper investigated the use of titanium dioxide sol-gel coatings to photo-catalyse red wine stains on wool fabrics. Coatings were produced by the hydrolysis and condensation of titanium butoxide (Ti(OC4H9)4) on the surface of wool fabrics after pad application. Coatings were partially converted to the anatase form of titanium dioxide by prolonged immersion in boiling water. The coating presence was confirmed using scanning electron microscopy, UVspectrophotometry and atomic force microscopy. Coated samples were measured for photo-catalytic activity by degrading red wine stains from the surface of the coated fabric. The level of photocatalysis was determined for each of the coating systems after 168 hours. Red wine stains were photo-catalysed and level of staining was reduced from the UV exposed surface of the coated wool fabric.

Bioactivating the surfaces of titanium by sol-gel process

In the present study, titanium (Ti) samples were surface-modified by titania (TiO₂), silica (SiO₂) and hydroxyapatite (HA) coatings using a sol-gel process. The bioactivity of the film-coated Ti samples was investigated by cell attachment and morphology study using human osteoblast-like SaOS-2 cells. Results of the cell attachment indicated that the densities of cell attachment on the surfaces of Ti samples were significantly increased by film coatings; the density of cell attachment on HA film-coated surface was higher than those on TiO₂ and SiO₂ film-coated surfaces. Cell morphology study showed that the cells attached, spread and grew well on the three kinds of film-coated surfaces. It can be concluded that the three kinds of film coatings can bioactivate the surfaces of Ti samples effectively. Overall, Ti sample with HA film-coated surface exhibited the best bioactivity.

Bioactive hydroxyapatite coating on titanium-niobium alloy through a sol-gel process

Hydroxyapatite (HA) was coated on the surface of a titanium-niobium (Ti-Nb) alloy by a sol-gel process. Triethyl phosphite and calcium nitrate were used as the phosphorus (P) and calcium (Ca) precursors respectively to prepare a Ca/P sol solution. The Ti-Nb alloy was dip-coated in the sol and heated at 600°C for 30 minutes. X-ray diffraction (XRD) analysis indicated the major phase constituent of the coating after heat treatment was HA. Scanning electron microscopy (SEM) observation showed that a few cracks were distributed on the HA coating. The in-vitro bioactivity of the HA coated Ti-Nb alloy was assessed using a cell culture of SaOS-2 osteoblast-like cells. The density of cell attachment was determined by MTT assay; the cell morphology was observed by SEM. Results indicated that the density of cell attachment on the surface of the Ti-Nb alloy was significantly increased by HA coating. Cell morphology observation showed that cells attached, spread and grew well on the HA coated surface. It can be concluded that the HA coating improved the in-vitro bioactivity of Ti-Nb alloy effectively.

Photochromic wool fabric by sol-gel coating

This thesis investigates the possibility of producing photochromic wool fabrics using a silica sol-gel coating method. Silicas made from sol-gel methods are uniquely suited to host photochromic dyes for developing colour-changing wool. The achieved photochromic effects have opened a new product area for fashion effects on wool textiles.

Synthesis of an Al/MgAl2O4 in situ metal matrix composite from silica gel

An aluminum/MgAl2O4 in situ metal matrix composite has been synthesized using silica gel containing B98% SiO2 in an Al–5Mg alloy. The thermodynamics and kinetics of MgAl2O4 formation have been discussed in detail. A transition phase of composition between MgO and MgAl2O4 has been detected in the SEM-EDS analysis of the particles extracted from the composite by a 25% NaOH solution. This confirms the gradual transformation of MgO to MgAl2O4 by the reaction 3SiO2(s)12MgO(s)14Al(l)-2MgAl2O4(s)13Si(l). The stoichiometry, n, of MgAl2O4 has been found to sustain close to 1 and the crystallite growth of MgAl2O4 has been stopped at DB30 nm in the composites held at 7501C up to 10 h.

Ion and solvent dynamics in gel electrolytes based on ethylene oxide grafted acrylate polymers

Multinuclear pulsed field gradient NMR measurements and rheological viscosity measurements were performed on three series of polymer gel electrolytes. The gels were based on a lithium salt electrolyte swollen into a copolymer matrix comprising an acrylate backbone and ethylene oxide side chains. In each series the side chains differed in length and number, but the acrylate-to-ethylene oxide ratio was kept constant. It was found that the self-diffusion coefficient of the cations was much lower than that of the anions, and that it decreased rapidly when the side chains got longer. In contrast, the self-diffusion coefficient of the anions was found to be independent of chain length. In the gel electrolytes, the diffusion coefficients of the solvent molecules are relatively constant despite an increased viscosity with increasing length of the side chains. However, in salt-free gels made for comparison, the diffusion coefficients of the solvent molecules decreased with increasing length of the side chains, which is consistent with an increased viscosity.

7Li NMR measurements of polymer gel electrolytes

Ion conducting polymer gels prepared from (ethylene oxide)_n grafted methacrylates, ethylene carbonate (EC), gamma butyrolactone (gBL), and lithium hexafluorophosphate are studied by means of nuclear magnetic resonance spectroscopy. This study shows that there are at least two possible lithium sites with different mobility. The lithium-ions with lower mobility dominate at room temperature, but this is changed as the temperature is increased. The NMR results also show that the ⁷Li spin–spin relaxation time decreases with increasing length of the grafted ethylene oxide side chains, indicating a stronger interaction between the polymer and the Li-ions, and hence, a lower mobility of the Li-ions.